Evolution of Dislocation Density During Tensile Deformation of BH220 Steel at Different Pre-strain Conditions
IR@NML: CSIR-National Metallurgical Laboratory, Jamshedpur
View Archive InfoField | Value | |
Title |
Evolution of Dislocation Density During Tensile Deformation of BH220 Steel at Different Pre-strain Conditions
|
|
Creator |
Seth, Prem Prakash
Das, Arpan Bar, H N Sivaprasad, S Basu, A Dutta, K |
|
Subject |
Materials Science
|
|
Description |
Tensile behavior of BH220 steel with different pre-strain conditions (2 and 8%) followed by bake hardening was studied at different strain rates (0.001 and 0.1/s). Dislocation densities of the deformed specimens were successfully estimated from x-ray diffraction profile analysis using the modified Williamson-Hall equation. The results indicate that other than 2% pre-strain the dislocation density increases with increase in pre-strain level as well as with strain rate. The decrease in the dislocation density in 2% pre-strain condition without any drop in strength value is attributed to the characteristic dislocation feature formed during pre-straining.
|
|
Publisher |
Springer, USA
|
|
Date |
2015
|
|
Type |
Article
PeerReviewed |
|
Relation |
http://apps.webofknowledge.com/full_record.do?product=UA&search_mode=GeneralSearch&qid=2&SID=S1AnDO8z54Fzm5VlBuU&page=1&doc=5&cacheurlFromRightClick=no
http://eprints.nmlindia.org/7260/ |
|
Identifier |
Seth, Prem Prakash and Das, Arpan and Bar, H N and Sivaprasad, S and Basu, A and Dutta, K (2015) Evolution of Dislocation Density During Tensile Deformation of BH220 Steel at Different Pre-strain Conditions. Journal of Materials Engineering and Performance, 24(7) (IF-0.998). pp. 2779-2783.
|
|