Strain mediated magnetoelectric coupling induced in (x) Bi0.5Na0.5TiO3-(1-x) MgFe2O4 composites
IR@NPL: CSIR-National Physical Laboratory, New Delhi
View Archive Info| Field | Value | |
| Title |
Strain mediated magnetoelectric coupling induced in (x) Bi0.5Na0.5TiO3-(1-x) MgFe2O4 composites
|
|
| Creator |
-, Manjusha
Yadav, K. L. Adhlakha, Nidhi Shah, Jyoti Kotnala, R. K. |
|
| Subject |
Physics
|
|
| Description |
Particulate composites of ferroelectric and ferrite phases having general formula (x) Bi0.5Na0.5TiO3-(1-x) MgFe2O4 (x= 0, 0.5, 0.6, 0.7, 0.8 and 1.0), equivalently denoted as (x) BNT-(1-x) MgFO were synthesized by solid state reaction method. From X-ray diffraction analysis, the structural transformation from tetragonal to rhombohedral corresponding to BNT phase was observed in composites with x= 0.5 to x= 0.8. Shifting of (012) BNT peak towards left (x= 0.5, 0.8) and right side (x= 0.6, 0.7) observed due to occupation of Bi3+ ions at interstitial and substitutional sites into host MgFO lattice respectively. BNT produced strain in MgFO lattice. Scanning electron micrographs show closely packed microstructure with grain size variations from 0.62 to 2.90 aem. The value of magnetoelectric (ME) coupling coefficient increases from 2.42 (x= 0.5) to 4.79 (x= 0.8) mV/cm. Oe due to strain produced in MgFO and BNT lattices.
|
|
| Publisher |
Elsevier
|
|
| Date |
2017-06-01
|
|
| Type |
Article
PeerReviewed |
|
| Format |
application/pdf
|
|
| Identifier |
http://npl.csircentral.net/2859/1/Strain%20mediated%20magnetoelectric%20coupling%20induced.pdf
-, Manjusha and Yadav, K. L. and Adhlakha, Nidhi and Shah, Jyoti and Kotnala, R. K. (2017) Strain mediated magnetoelectric coupling induced in (x) Bi0.5Na0.5TiO3-(1-x) MgFe2O4 composites. Physica B: Condensed Matter, 514. pp. 41-50. ISSN 0921-4526 |
|
| Relation |
http://npl.csircentral.net/2859/
|
|