A Comparative Analysis of BaTiO3/(Ba,Sr)TiO3 and BaTiO3/(Ba,Sr)TiO3/SrTiO3 Artificial Superlattices via Raman Spectroscopy
IR@NPL: CSIR-National Physical Laboratory, New Delhi
View Archive InfoField | Value | |
Title |
A Comparative Analysis of BaTiO3/(Ba,Sr)TiO3 and BaTiO3/(Ba,Sr)TiO3/SrTiO3 Artificial Superlattices via Raman Spectroscopy
|
|
Creator |
Maslova, Olga Aleksandrovna
Yuzyuk, Yuri Ivanovich Ortega, Nora Kumar, Ashok Katiyar, Ram Barannikova, Svetlana Aleksandrovna |
|
Subject |
Materials Science
|
|
Description |
BaTiO3/Ba50Sr50TiO3 and BaTiO3/Ba50Sr50TiO3/SrTiO3 superlattices are characterized via Raman spectroscopy. Special attention is paid to a comprehensive analysis of their polarized Raman spectra, especially, within a soft mode (E(1TO)) range. The shift of E(1TO) soft mode is found to be more pronounced for BaTiO3/Ba50Sr50TiO3/SrTiO3 sample than for BaTiO3/Ba50Sr50TiO3, presumably owing to stronger 2D compression of BT layers and abruptly increased temperature of transition from ferroelectric to paraelectric phase.
|
|
Publisher |
Associação Brasileira de Metalurgia e Materiais (ABM)
|
|
Date |
2019
|
|
Type |
Article
PeerReviewed |
|
Format |
application/pdf
|
|
Identifier |
http://npl.csircentral.net/4096/1/A%20Comparative%20Analysis%20of.pdf
Maslova, Olga Aleksandrovna and Yuzyuk, Yuri Ivanovich and Ortega, Nora and Kumar, Ashok and Katiyar, Ram and Barannikova, Svetlana Aleksandrovna (2019) A Comparative Analysis of BaTiO3/(Ba,Sr)TiO3 and BaTiO3/(Ba,Sr)TiO3/SrTiO3 Artificial Superlattices via Raman Spectroscopy. Materials Research , 22 (1). UNSP e20180389- e20180394. ISSN 1516-1439 |
|
Relation |
http://npl.csircentral.net/4096/
|
|