Permeability and dust filtration behaviour of porous SiC ceramic candle filter
IR@CGCRI: CSIR-Central Glass and Ceramic Research Institute, Kolkata
View Archive Info| Field | Value | |
| Title |
Permeability and dust filtration behaviour of porous SiC ceramic candle filter
|
|
| Creator |
Das, Dulal
Kayal, Nijhuma |
|
| Subject |
Engineering Materials
|
|
| Description |
Porous SiC candle filter (similar to 660 mm L and 75 mm OD) were fabricated by ramming process using commercially available SiC powder (d(50) = 212 mu m), with and without alumina and small amount (3 wt %) of clay as the major binder phase additives, following heat treatment at 1400 degrees C in air. Depending on the composition, porosity of the candle filters varied from 36 to 39 vol% and C-ring strength varied from 15 to 23 MPa. The air permeability and dust filtration efficiency of the candle filter were evaluated using laboratory made test set up. At room temperature, Darcian (k(1)) and non-Darcian (k(2)) permeability parameters varied from 1.9 to 2.2 x 10(-12) m(2) and 5.4-9.72 x 10(-8) m, respectively. Airborne fly ash particle filtration tests showed good performance of SiC candle filter with filtration efficiency of >97%. (C) 2020 Elsevier Ltd. All rights reserved.
|
|
| Publisher |
Elsevier
|
|
| Date |
2021
|
|
| Type |
Article
PeerReviewed |
|
| Format |
application/pdf
|
|
| Identifier |
http://cgcri.csircentral.net/5202/1/dulal.pdf
Das, Dulal and Kayal, Nijhuma (2021) Permeability and dust filtration behaviour of porous SiC ceramic candle filter. Materials Today-Proceedings, 39 (4). pp. 1235-1240. ISSN 2214-7853 |
|
| Relation |
http://cgcri.csircentral.net/5202/
|
|