Improvement of the mechanical strength of alumina performs by coating with montmorillonite / LDH ge

IR@NEIST: CSIR-North East Institute of Science and Technology, Jorhat

View Archive Info
 
 
Field Value
 
Title Improvement of the mechanical strength of alumina performs by coating with montmorillonite / LDH ge
 
Creator MISHRE , M
BORA , J J
GOSWAMEE, R L
 
Subject Material Science
 
Description AcompositematerialwaspreparedfrommontmorilloniteandMg–AlLDH.Theseoppositelychargedparticles form thixotropic gels with distinctflow and micro-structural properties. The stability of the gel was dependent on the montmorillonite/LDH ratio. Novel advanced ceramic materials were designed by coating ceramic preforms with these gels. During calcination these gels decompose to metal oxides, aluminosilicates and spinel. On calcination at 1400 °C, MgO formed from the LDH of the gel reacted with the aluminosilicate formed by the decomposition of the montmorillonite. A non-porous dense matrix was formed with well grown crystals of MgAl2O4 spinel embedded in the aluminosilicate matrix. When the ceramic preforms like porous alumina tube were dip coated with the gel andfired at 1400 °C, the molten aluminosilicate infiltrated into the pores of the aluminum oxide carrying spinel crystals. These spinel crystals settled in the pores and increased the mechanical strength of the alumina tubes. The compressive strength was increased by around 94% and the mechanical extension in the z-direction in the coated body by 4% compared to the uncoated counterpart.
 
Date 2011
 
Type Article
PeerReviewed
 
Format application/pdf
 
Identifier http://neist.csircentral.net/113/1/2933.pdf
MISHRE , M and BORA , J J and GOSWAMEE, R L (2011) Improvement of the mechanical strength of alumina performs by coating with montmorillonite / LDH ge. Applied Clay Science , 53 (1). pp. 8-14.
 
Relation http://neist.csircentral.net/113/