Improved anode performance of thermally treated SiO/C composite with an organic solution mixture
IR@CECRI: CSIR-Central Electrochemical Research Institute, Karaikudi
View Archive InfoField | Value | |
Title |
Improved anode performance of thermally treated SiO/C
composite with an organic solution mixture
|
|
Creator |
Doh, C.H.
Shin, H.M. Kim, D.H. Ha, Y.C. Jin, B.S. Kim, H.S. Moon, S.I. Veluchamy, A. |
|
Subject |
Electroorganic
Lithium batteries Electrochemical Power Sources |
|
Description |
made in the form of a slurry using a simple solution mixture consisting of propylene carbonate (PC) and acetone (AC) and then heat
treated. Cycle life study of the pristine composite and heat treated organic slurry composite showed the charge capacity values as 318
and 500 mAh g�1, respectively at 100th cycle. Analysis of change of delithiation capacity with cycling and delithiation current between
0.3 and 0.6 V from cyclic voltammogram (CV) along with scanning electron microscope (SEM) and X-ray diffraction (XRD) of the electrodes/
composites leads to conclude thermal processing of the organic slurry treated pristine composite converts dispersed active materials
of the pristine composite into a compact structure trapped/wrapped with carbon particles (Cx, x varies from 1 to 3) providing
apparently a resistor like behaviour and makes the anode deliver a stable reversible capacity with cycling.
|
|
Publisher |
Elsevier B.V.
|
|
Date |
2008
|
|
Type |
Article
PeerReviewed |
|
Format |
application/pdf
|
|
Identifier |
http://cecri.csircentral.net/94/1/035-2008.pdf
Doh, C.H. and Shin, H.M. and Kim, D.H. and Ha, Y.C. and Jin, B.S. and Kim, H.S. and Moon, S.I. and Veluchamy, A. (2008) Improved anode performance of thermally treated SiO/C composite with an organic solution mixture. Electrochemistry Communications, 10 (2). pp. 233-237. |
|
Relation |
http://cecri.csircentral.net/94/
|
|