In situ electron beam irradiated rapid growth of bismuth nanoparticles in bismuth-based glass dielectrics at room temperature
IR@CGCRI: CSIR-Central Glass and Ceramic Research Institute, Kolkata
View Archive InfoField | Value | |
Title |
In situ electron beam irradiated rapid growth of bismuth nanoparticles in bismuth-based glass dielectrics at room temperature
|
|
Creator |
Singh, Shiv Prakash
Karmakar, Basudeb |
|
Subject |
Glass
Electronics |
|
Description |
In this study, in situ control growth of bismuth nanoparticles (Bi(0) NPs) was demonstrated in bismuth-based glass dielectrics under an electron beam (EB) irradiation at room temperature. The effects of EB irradiation were investigated in situ using transmission electron microscopy (TEM), selected-area electron diffraction and high-resolution transmission electron microscopy. The EB irradiation for 2-8 min enhanced the construction of bismuth nanoparticles with a rhombohedral structure and diameter of 4-9 nm. The average particle size was found to increase with the irradiation time. Bismuth metal has a melting point of 271 A degrees C and this low melting temperature makes easy the progress of energy induced structural changes during in situ TEM observations. This is a very useful technique in nano-patterning for integrated optics and other applications.
|
|
Publisher |
Springer
|
|
Date |
2011-09
|
|
Type |
Article
PeerReviewed |
|
Format |
application/pdf
application/pdf |
|
Identifier |
http://cgcri.csircentral.net/354/1/J_Nanopart_Res_13_(2011)_3599%E2%80%933606.pdf
http://cgcri.csircentral.net/354/3/SPS%2DJ_Nano_Part_Research.pdf Singh, Shiv Prakash and Karmakar, Basudeb (2011) In situ electron beam irradiated rapid growth of bismuth nanoparticles in bismuth-based glass dielectrics at room temperature. Journal of Nanoparticle Research, 13 (9). pp. 3599-3606. ISSN 1388-0764 |
|
Relation |
http://cgcri.csircentral.net/354/
|
|