Synthesis and characterization of ZnAl2O4 precursor in relation to different basic media

IR@CGCRI: CSIR-Central Glass and Ceramic Research Institute, Kolkata

View Archive Info
 
 
Field Value
 
Title Synthesis and characterization of ZnAl2O4 precursor in relation to different basic media
 
Creator Adhikari, Uday Bhanu
Saha, M B
Parya, T K
 
Subject Crystal Chemistry, Thermodynamics, Phase Equilibria
 
Description The role of different basic media for the preparation of Zn-Al based hydroxy compounds; leading to the formation of ZnAl2O4 spinet at low temperature was investigated. Nitrate salts of respective cations with molar ratio for ZnO : Al2O3 as 1 : 1 were used for coprecipitation. DTA, TGA, XRD, IR spectroscopy and SEM technique were utilised for characterization of the precursor hydroxy compounds as well as the final products obtained by heat treatment of the hydroxy compounds at different temperatures. It had been found that spinet formation was very much influenced by the nature of mixed hydroxide precursors obtained by using different basic media. The thermal treatment of the coprecipitated gel powders led to the formation of ZnAl2O4 at relatively low temperature (500degrees). Mixed hydroxide gel powder obtained by using NH4OH-hexamethylene tetramine (HMT) as basic medium was observed to exhibit best results so far as spinet formation at low temperature was concerned.
 
Date 2004-08
 
Type Article
PeerReviewed
 
Identifier Adhikari, Uday Bhanu and Saha, M B and Parya, T K (2004) Synthesis and characterization of ZnAl2O4 precursor in relation to different basic media. JOURNAL OF THE INDIAN CHEMICAL SOCIETY , 81 (8). pp. 674-679. ISSN 0019-4522
 
Relation http://cgcri.csircentral.net/436/