Effects of State Change of Liquid Crystalline Polymer on Dynamic Visco-Elasticity of its Blends with Polyethylene-Terephthalate
IR@AMPRI: CSIR-Advanced Materials and Processes Research Institute, Bhopal
View Archive Info| Field | Value | |
| Title |
Effects of State Change of Liquid Crystalline Polymer on Dynamic Visco-Elasticity of its Blends with Polyethylene-Terephthalate
|
|
| Creator |
Dr., S A R Hashmi
Dr., Takeshi Kitano |
|
| Subject |
Polymeric Materials
|
|
| Description |
The dynamic viscoelastic properties of liquid crystalline polymer (LCP) and polyethylene terephthalate (PET)
blends were studied at two different temperatures: 265°C at which LCP was in solid state and 285°C at which LCP was in molten state. The PET was in molten state at both the temperatures. The storage modulus, G’, loss modulus, G’’, dynamic viscosity, h’, of blends with different compositions were evaluated and compared. The morphology of these samples was studied using scanning electron microscope, which exhibited composition dependency. A maxima was observed in the viscosity versus composition plot corresponding to 90/10 LCP/PET blend at 285°C. The G’ versus G’’ plots demonstrated the composition dependency of LCP/PET blends
|
|
| Date |
2007
|
|
| Type |
Article
PeerReviewed |
|
| Identifier |
Dr., S A R Hashmi and Dr., Takeshi Kitano (2007) Effects of State Change of Liquid Crystalline Polymer on Dynamic Visco-Elasticity of its Blends with Polyethylene-Terephthalate. Applied Rheology, 17 (6). pp. 64510-1. ISSN 1430-6395
|
|
| Relation |
http://ampri.csircentral.net/19/
|
|