Synthesis, consolidation and dielectric properties of BLT ceramics processed by M-PVA gel ignition technique
IR@CGCRI: CSIR-Central Glass and Ceramic Research Institute, Kolkata
View Archive Info| Field | Value | |
| Title |
Synthesis, consolidation and dielectric properties of BLT ceramics processed by M-PVA gel ignition technique
|
|
| Creator |
Roy, S
Singh, S Kumar, P Bysakh, Sandip Prasad, V V Bhanu |
|
| Subject |
Engineering Materials
|
|
| Description |
Polycrystalline samples of lanthanum modified bismuth titanate ceramics with composition Bi3.25La0.75Ti3O12 (BLT) were prepared at three different sintering temperatures (1050, 1100 and 1150 degrees C) using M-PVA gel ignition technique. The samples were characterised for structural and electrical properties. A significant amount of as burnt BLT powder was found to be crystalline in nature having a yellowish colour. Very fine BLT nanoparticles were characterised by TEM analysis. Single phase with orthorhombic crystal structure was observed for all the samples, confirmed by X-ray analysis. Dielectric properties were studied as a function of frequency and temperature. More than 95% relative density was observed for all the three sintered samples. The sample sintered at 1100 degrees C showed highest dielectric constant and relative density and lowest loss.
|
|
| Publisher |
Maney Publishing
|
|
| Date |
2013-07
|
|
| Type |
Article
PeerReviewed |
|
| Format |
application/pdf
|
|
| Identifier |
http://cgcri.csircentral.net/2167/1/roy2013.pdf
Roy, S and Singh, S and Kumar, P and Bysakh, Sandip and Prasad, V V Bhanu (2013) Synthesis, consolidation and dielectric properties of BLT ceramics processed by M-PVA gel ignition technique. Advances in Applied Ceramics, 112 (5). pp. 263-269. ISSN 1743-6753 |
|