Effect of acidity and porosity changes of dealuminated mordenites on n-hexane isomerization
IR@IIP: CSIR-Indian Institute of Petroleum, Dehradun
View Archive InfoField | Value | |
Creator |
Viswanadham,N
Dixit,Lalji Gupta,J.K Garg,M.O |
|
Date |
2009-07-01T11:14:53Z
2009-07-01T11:14:53Z 2009-07-01T11:14:53Z |
|
Identifier |
Journal of Molecular Catalysis A: Chemical 258 (2006) 15–21
http://hdl.handle.net/123456789/285 |
|
Description |
A series of dealuminated mordenite samples was prepared and tested for their activity in n-hexane hydroisomerization reaction. The samples
were thoroughly characterized by XRD, microcalorimetry, and adsorption measurement to obtain surface area, pore volume and pore size distribution.
Both strong acidity ( HNH3 > 100 kJ/mol) and micropore volume (0–20 A° ) of the mordenite were increased during the initial stage
of dealumination. Further dealumination caused very little or negligible improvement in the catalytic properties. Among the various catalysts
prepared, the catalyst dealuminated by steaming at 673 K, followed by acid leaching with 2N HNO3 (S2-HM) exhibited highest amount of strong
acidity and isomer yields in n-hexane conversion. The selectivity to di-branched isomers was continuously increased with dealumination.
Keywords: Mordenite; Steaming; Dealumination; Strong acidity; Micropore; Isomer yield
|
|
Language |
en_US
|
|
Subject |
Dealumination
Mordenite Isomer yield Steaming |
|
Title |
Effect of acidity and porosity changes of dealuminated mordenites on n-hexane isomerization
|
|