Electrodeposition of Zinc from Low Temperature Molten Salt Electrolyte: Part II - Imidazole – Alcl3/Zinc Chloride LTMS
IR@CECRI: CSIR-Central Electrochemical Research Institute, Karaikudi
View Archive InfoField | Value | |
Title |
Electrodeposition of Zinc from Low Temperature
Molten Salt Electrolyte: Part II - Imidazole –
Alcl3/Zinc Chloride LTMS
|
|
Creator |
Shanmugasigamani, S.
Thangavelu , PR. Srinivasan, K.N. Selvam, M. |
|
Subject |
Industrial Metal Finishing
|
|
Description |
Low Temperature Molten salts (LTMS) have a
number of applications in metal finishing including electrolytic deposition and anodic processes like polishing and colouring. Imidazolium, pyridinium and choline based cations are normally used in LTMS [1-5]. Zinc deposition was carried out from imidazole - AlCl3 / ZnCl2 LTMS electrolyte at temperature < 100º C and the mole ratio was optimized in our research. Surface morphology of electrodeposited coatings was characterized by SEM and XRD. Cathodic and anodic current efficiencies of Imidazole – AlCl3 / ZnCl2 LTMS were evaluated.
|
|
Date |
2014-02-21
|
|
Type |
Article
PeerReviewed |
|
Format |
application/pdf
|
|
Identifier |
http://cecri.csircentral.net/3073/1/015-2014.pdf
Shanmugasigamani, S. and Thangavelu , PR. and Srinivasan, K.N. and Selvam, M. (2014) Electrodeposition of Zinc from Low Temperature Molten Salt Electrolyte: Part II - Imidazole – Alcl3/Zinc Chloride LTMS. International Journal of Engineering Research & Technology (IJERT), 3 (2). pp. 757-761. ISSN ISSN: 2278-0181 |
|
Relation |
http://www.ijert.org
http://cecri.csircentral.net/3073/ |
|