Effect of sillimanite particle Reinforcement on the dry sliding wears behavior of Aluminum alloy composite.
IR@AMPRI: CSIR-Advanced Materials and Processes Research Institute, Bhopal
View Archive InfoField | Value | |
Title |
Effect of sillimanite particle Reinforcement on the dry sliding wears behavior of Aluminum alloy composite.
|
|
Creator |
Yadav, M.S
D.P., Mondal Dr., A H Yegneshwaran Jha, A.K B K , Prasad DasGupta, R |
|
Subject |
Metal Matrix Composites
Tribology |
|
Description |
The effect of sillimanite reinforcement on the dry sliding wear behaviour of aluminium silicon alloy (BS LM6)
composite was investigated using a pin-on-disc sliding wear test machine. The composite specimens were prepared
using the liquid metallurgy technique and 10 wt-% of sillimanite particles were incorporated in the matrix alloy.
Sliding wear tests were conducted at applied pressures between 0.2 and 1.6 MPa and speeds of 1.89, 3.96 and
5.55 m s
1
. The matrix alloy was also prepared and tested under identical conditions in order to enable comparison.
It was observed that the sillimanite reinforced composite exhibited a lower wear rate than the matrix alloy. Increase
in applied load increased the wear rate while increase in speed exhibited the reverse effect. The seizure pressure of the
composite was signi®cantly higher than that of the matrix alloy. The temperature rise near the contacting surface
and the coef®cient of friction were less in the composite than in the matrix alloy. SEM micrographs of the worn
surface and subsurface were used to predict the nature of the wear mechanism.
|
|
Date |
2003-03-01
|
|
Type |
Article
PeerReviewed |
|
Format |
application/pdf
|
|
Identifier |
http://ampri.csircentral.net/1044/1/10.pdf
Yadav, M.S and D.P., Mondal and Dr., A H Yegneshwaran and Jha, A.K and B K , Prasad and DasGupta, R (2003) Effect of sillimanite particle Reinforcement on the dry sliding wears behavior of Aluminum alloy composite. Materials Science and Technology. |
|
Relation |
http://ampri.csircentral.net/1044/
|
|