A Contribution to the Service Failure of Large Chilled Iron Rolls due to Fatigue
IR@NML: CSIR-National Metallurgical Laboratory, Jamshedpur
View Archive Info| Field | Value | |
| Title |
A Contribution to the Service Failure of Large Chilled Iron Rolls due to Fatigue
|
|
| Creator |
Shimoda, Hideo
Onodera, S |
|
| Subject |
Metallurgy
|
|
| Description |
A case of service rupture of chilled iron roll due to fatigue is presented with condition of rupture, invest-igation of the cause, and remedial result through remo-delling.
As a result of this, it is suggested that service strength of chilled iron rolls should be considered
through fatigue, and that standard size is not necessar-ily of sufficient strength from this point of view ; a remark for the prevention of service failures in existent mills, and to which reference is desired to make in bui-lding new mills
|
|
| Date |
1953-02
|
|
| Type |
Conference or Workshop Item
PeerReviewed |
|
| Format |
application/pdf
|
|
| Identifier |
http://eprints.nmlindia.org/3364/1/17-30.PDF
Shimoda, Hideo and Onodera, S (1953) A Contribution to the Service Failure of Large Chilled Iron Rolls due to Fatigue. In: Symposium on Industrial Failure of Engineering Metals & Alloys, Feb. 5-7, 1953, NML, Jamshedpur. |
|
| Relation |
http://eprints.nmlindia.org/3364
http://eprints.nmlindia.org/3364/ |
|