Microstructures and Textures of Hot Rolled and Hot Rolled-Normalized 2.9 % Silicon Steel Sheets
IR@NML: CSIR-National Metallurgical Laboratory, Jamshedpur
View Archive Info| Field | Value | |
| Title |
Microstructures and Textures of Hot Rolled and Hot Rolled-Normalized 2.9 % Silicon Steel Sheets
|
|
| Creator |
Humane, M M
Thool, K S Minz, R K Kestens, L A I |
|
| Subject |
Metallurgy
Metallurgical Techniques |
|
| Description |
Effect of hot rolling and effect of hot rolled-normalizing on microstructures and textures of silicon steel sheets were investigated. In hot rolled steel sheets, fine elongated grains and etch pits were observed. , and were strong orientations at the core of steel sheet. At surface and subsurface, and orientations were dominant orientations. In hot rolled-normalized steel sheets, coarse elongated grains and randomly distributed etch pits were observed. Volume fraction (%) of orientation was found to be decreasing from core to surface, similar trend was found for and orientations. & orientations are the dominant orientations at the surface. Volume fraction (%) of is more than Goss at the surface.
|
|
| Publisher |
Springer India
|
|
| Date |
2015-06
|
|
| Type |
Article
PeerReviewed |
|
| Relation |
http://apps.webofknowledge.com/full_record.do?product=UA&search_mode=GeneralSearch&qid=1&SID=R2guq97BWyY5sM9LYpE&page=1&doc=19&cacheurlFromRightClick=no
http://eprints.nmlindia.org/7287/ |
|
| Identifier |
Humane, M M and Thool, K S and Minz, R K and Kestens, L A I (2015) Microstructures and Textures of Hot Rolled and Hot Rolled-Normalized 2.9 % Silicon Steel Sheets. Transactions of the Indian Institute of Metals, 68(3) (IF- 0.502). pp. 371-381.
|
|