A Thermal Cycling Route for Processing Nano-grains in AISI 316L Stainless Steel for Improved Tensile Deformation Behaviour

IR@NML: CSIR-National Metallurgical Laboratory, Jamshedpur


Field	Value

Title	A Thermal Cycling Route for Processing Nano-grains in AISI 316L Stainless Steel for Improved Tensile Deformation Behaviour

Creator	Nanda, T Ravi Kumar, B Singh, V

Subject	Materials Charcterization

Description	The present work significantly improved the mechanical strength of AISI 316L stainless steel by producing nano-sized grains. Steel was subjected to cold rolling followed by repetitive thermal cycling to produce ultra-fine/nano-sized grains. The optimum processing parameters including extent of cold deformation, annealing temperature for thermal cycling, soaking period during each thermal cycle, and number of thermal cycles were determined through a systematic step-by-step procedure. After conducting thermal cycling under optimum conditions, a significant amount of grain size reduction was achieved. The effect of nano-sized grains on tensile deformation behavior was analysed. High cold deformation resulted in increased amount of stored strain energy. The stored strain energy accelerated the re-crystallisation kinetics during the thermal cycling process. Every thermal cycle resulted in irregular dispersal of stored energy. This irregular dispersal of stored energy favoured recrystallisation rather than grain growth and led to refinement of grains, in the absence of strain induced martensite. Repetitive thermal cycling promoted grain refinement and resulted in very significant grain size reduction with resultant grain size in the range of 800-1200 nm as compared to initial size of 90-120 mu m. The resultant microstructure improved tensile strength by 106.8 per cent, from 590 MPa to 1220 MPa.

Publisher	Defence Scientific Information Documentation Centre

Date	2016

Type	Article PeerReviewed

Relation	http://publications.drdo.gov.in/ojs/index.php/dsj/article/view/9948 http://eprints.nmlindia.org/7485/

Identifier	Nanda, T and Ravi Kumar, B and Singh, V (2016) A Thermal Cycling Route for Processing Nano-grains in AISI 316L Stainless Steel for Improved Tensile Deformation Behaviour. Defence Science Journal, 66(5) (IF-0.500). pp. 529-535.