Magnetoelectric dipole interaction in RF-magnetron sputtered (1-x) BiFeO3-xBaTiO(3) thin films
IR@NPL: CSIR-National Physical Laboratory, New Delhi
View Archive InfoField | Value | |
Title |
Magnetoelectric dipole interaction in RF-magnetron sputtered (1-x) BiFeO3-xBaTiO(3) thin films
|
|
Creator |
Gupta, Rekha
Shah, Jyoti Chaudhary, Sujeet Kotnala, R. K. |
|
Subject |
Physical Chemistry
|
|
Description |
Optimum composition with improved ferroelectric polarization and magnetization of multiferroic thin films (1 - x) BiFeO3-xBaTiO(3) (x = 0, 0.1, 0.2 and 0.3) prepared by RF-magnetron sputtering have been analyzed for their multi functionality. Composite film optimized for x = 0.1, showed shift in dielectric loss peak toward lower frequency by 0.3 MHz with applied magnetic field. It confirms electric dipoles are brought in equilibrium condition at lower frequency due to active magnetoelectric dipole interaction. The film showed remnant electric polarization (2Pr) of 11 mu C/cm(2) and saturation magnetization of 3.75 emu/g. Room temperature transverse magnetoelectric coupling coefficient (alpha(ME)) similar to 124 mV/cm Oe has been observed for x = 0.1 composite thin film. The observed properties are very useful to exploit room temperature functional spintronic devices.
|
|
Publisher |
Elsevier
|
|
Date |
2015-07-25
|
|
Type |
Article
PeerReviewed |
|
Format |
application/pdf
|
|
Identifier |
http://npl.csircentral.net/1891/1/198.pdf
Gupta, Rekha and Shah, Jyoti and Chaudhary, Sujeet and Kotnala, R. K. (2015) Magnetoelectric dipole interaction in RF-magnetron sputtered (1-x) BiFeO3-xBaTiO(3) thin films. Journal of Alloys and Compounds, 638. pp. 115-120. ISSN 0925-8388 |
|
Relation |
http://npl.csircentral.net/1891/
|
|