Extremely fast Au-Ag alloy-dealloy associated reversible plasmonic modifications in SiO2 films
IR@CGCRI: CSIR-Central Glass and Ceramic Research Institute, Kolkata
View Archive Info| Field | Value | |
| Title |
Extremely fast Au-Ag alloy-dealloy associated reversible plasmonic modifications in SiO2 films
|
|
| Creator |
Pramanik, Sourav
Chattopadhyay, Shreyasi Das, Jugal Kishore Manju, Unnikrishnan De, Goutam |
|
| Subject |
Engineering Materials
|
|
| Description |
We report a unique alloy-dealloy phenomenon of Au-Ag nanoparticles inside SiO2 films with clear plasmonic modifications between the absorptions of Ag (similar to 415 nm) and Au (similar to 524 nm). An Au-Ag (1 : 1) alloy nanoparticles (average size: 4.5 nm)-incorporated transparent SiO2 film is prepared on a glass substrate using mercaptosuccinic acid capped Au nanoparticles and Ag+ co-doped hybrid sol. The Au-Ag (1 : 1) alloy-originated plasmon band (465 +/- 1 nm) is gradually red-shifted with increasing temperature (50 to 400 degrees C) due to the partial oxidation of Ag, causing a systematic modification of the alloy composition. The 1 : 1 alloy, however, reverted very quickly, showing its original plasmon band in the presence of a small amount of H-2 due to re-reduction of the oxidized Ag and instantaneous re-alloying. During the Ag oxidation, the Si-OH groups associated with the embedded SiO2 matrix exchange Ag+ to form Ag-O-Si linkages; they subsequently release Ag very quickly in H-2 and dissolve again into the parent alloy. As a result, the films exhibit reversible and rapid optical changes while cycling in 0.1% to 1% H-2 (balance Ar) and air in the temperature range from 50 to 400 degrees C. This unique reversible alloy-dealloy phenomenon clearly demonstrates the mechanism of plasmonic modification associated with Au-Ag nanoparticles embedded in the sol-gel SiO2 film matrix.
|
|
| Publisher |
Royal Society of Chemistry
|
|
| Date |
2016-01
|
|
| Type |
Article
PeerReviewed |
|
| Format |
application/pdf
|
|
| Identifier |
http://cgcri.csircentral.net/3632/1/sourav.pdf
Pramanik, Sourav and Chattopadhyay, Shreyasi and Das, Jugal Kishore and Manju, Unnikrishnan and De, Goutam (2016) Extremely fast Au-Ag alloy-dealloy associated reversible plasmonic modifications in SiO2 films. Journal Of Materials Chemistry C, 4 (16). pp. 3571-3580. ISSN 2050-7526 |
|
| Relation |
http://cgcri.csircentral.net/3632/
|
|