Effect of Processing Parameters on Thermal Cycling Behavior of Al2O3-Al2O3 Brazed Joints
IR@CGCRI: CSIR-Central Glass and Ceramic Research Institute, Kolkata
View Archive Info| Field | Value | |
| Title |
Effect of Processing Parameters on Thermal Cycling Behavior of Al2O3-Al2O3 Brazed Joints
|
|
| Creator |
Dandapat, Nandadulal
Ghosh, Sumana Guha, Bichitra Kumar Datta, Someswar Balla, Vamsi Krishna |
|
| Subject |
Engineering Materials
|
|
| Description |
In the present study, alumina ceramics were active metal brazed at different temperatures ranging from 1163 K to 1183 K (890 A degrees C to 910 A degrees C) using TICUSIL (68.8Ag-26.7Cu-4.5Ti in wt pct) foil as filler alloy of different thicknesses. The brazed joints were subjected to thermal cycling for 100 cycles between 323 K and 873 K (50 A degrees C and 600 A degrees C). The microstructural and elemental composition analysis of the brazed joints were performed by scanning electron microscopy (SEM) and energy dispersive X-ray (EDX) before and after thermal cycling. Helium (He) leak test and brazing strength measurement were also conducted after thermal cycling for 100 cycles. The joint could withstand up to 1 x 10(-9) Torr pressure and brazing strength was higher than 20 MPa. The experimental results demonstrated that joints brazed at the higher temperature with thinner filler alloy produced strong Al2O3-Al2O3 joints.
|
|
| Publisher |
Springer
|
|
| Date |
2016-10
|
|
| Type |
Article
PeerReviewed |
|
| Format |
application/pdf
|
|
| Identifier |
http://cgcri.csircentral.net/3817/1/guha.pdf
Dandapat, Nandadulal and Ghosh, Sumana and Guha, Bichitra Kumar and Datta, Someswar and Balla, Vamsi Krishna (2016) Effect of Processing Parameters on Thermal Cycling Behavior of Al2O3-Al2O3 Brazed Joints. Metallurgical and Materials Transactions B, 47 (5). pp. 2946-2953. ISSN 1073-5615 |
|
| Relation |
http://cgcri.csircentral.net/3817/
|
|