Effect of reverse austenitic transformation on mechanical property and associated texture evolution in AISI 316 austenitic stainless steel processed by low temperature rolling and annealing
IR@NML: CSIR-National Metallurgical Laboratory, Jamshedpur
View Archive Info| Field | Value | |
| Title |
Effect of reverse austenitic transformation on mechanical property and associated texture evolution in AISI 316 austenitic stainless steel processed by low temperature rolling and annealing
|
|
| Creator |
Chattopadhyay, S
Anand, G Ghosh Chowdhury, S Manna, I |
|
| Subject |
Mechanical Engineering
|
|
| Description |
The tensile behaviour of austenitic stainless steel after cryorolling and subsequent annealing has been reported. The defect structures generated during cryorolling, lead to the formation of alpha' and epsilon-martensite. Subsequent annealing leads to the formation of refined austenitic grains surrounded by martensitic islands. These martensitic islands consist of alpha' phase only. The dislocation-martensite interaction leads to discontinuous yielding for high Ultimate Tensile Strength (UTS)/Yield Strength (YS) ratio. In case of annealing at 923 K (650 degrees C) for 10 min after 30% cryorolling leads to nearly 30% untransformed martensite whereas only 7% martensite remains after annealing for 1 h. The effect of remnant martensite on tensile behaviour leading to yield plateau has been discussed in this work. It can be noticed that sample with 20% cryo rolling and annealed at 650 degrees C for 1 h shows higher YS (721 MPa) with YS/UTS ratio of 0.79 and similar to 18% uniform elongation. Sample with 30% cryo rolling and annealed at 650 degrees C for 1 h shows YS of 305 MPa with YS/UTS ratio of 0.27 and uniform elongation of similar to 24%. Therefore, 20% cryo rolled and annealed at 650 degrees C for 1 h has the best combination of mechanical properties.
|
|
| Publisher |
Elsevier
|
|
| Date |
2018
|
|
| Type |
Article
PeerReviewed |
|
| Relation |
https://doi.org/10.1016/j.msea.2018.07.087
http://eprints.nmlindia.org/7755/ |
|
| Identifier |
Chattopadhyay, S and Anand, G and Ghosh Chowdhury, S and Manna, I (2018) Effect of reverse austenitic transformation on mechanical property and associated texture evolution in AISI 316 austenitic stainless steel processed by low temperature rolling and annealing. Materials Science And Engineering A-Structural Materials Properties Microstructure And Processing, 734 (IF-4.014). pp. 139-148.
|
|