Magnetoelectric coupling-induced anisotropy in multiferroic nanocomposite (1-x)BiFeO3-xBaTiO(3)
IR@NPL: CSIR-National Physical Laboratory, New Delhi
View Archive Info| Field | Value | |
| Title |
Magnetoelectric coupling-induced anisotropy in multiferroic nanocomposite (1-x)BiFeO3-xBaTiO(3)
|
|
| Creator |
Gupta, Rekha
Shah, Jyoti Chaudhary, Sujeet Singh, Sukhbeer Kotnala, Ravinder K. |
|
| Subject |
Chemistry
Materials Science Nanoscience/ Nanotechnology |
|
| Description |
Nanocomposite (1 - x)BiFeO3-xBaTiO(3) for x = 0.1, 0.2 and 0.3 compositions were prepared by sol-gel technique. X-ray diffractograms confirmed the formation of desired crystallographic phase of the composite. The average particle size was determined 75, 128 and 150 nm for x = 0.1, 0.2 and 0.3 samples by HRTEM measurement. Magnetic, dielectric and magnetoelectric response has been investigated to find out the magnetoelectric (ME) coupling at atomic scale mixing of the two phases. For effective ME coupling nanoscale synthesis provided large surface area and subsequently induced magnetic anisotropy in the sample. The computed value of magnetic anisotropy constant 4.8 x 10(3) erg/cm(3) was found to be maximum for x = 0.1 composition. It is believed that the anisotropy is being induced by ME coupling which changes with the composition. Correlated magnetic and dielectric transition temperatures were determined as an evidence of ME coupling in the material. To confirm the ME coupling room-temperature ME coupling coefficient (alpha) was calculated using dynamic method which was observed to have a maximum value of 2.74 mV/cmOe for x = 0.1 confirming the presence of room-temperature ME coupling in the nanocomposite. Spin flipping behaviour has been confirmed by ZFC-FC measurements at low temperature while the coercivity was found to be almost constant. Significantly, controlled coercivity behaviour has been correlated to the presence of ME coupling in the composite material, which can be very useful in memory device and spintronic application.
|
|
| Publisher |
Springer Verlag
|
|
| Date |
2013-09-26
|
|
| Type |
Article
PeerReviewed |
|
| Format |
application/pdf
|
|
| Identifier |
http://npl.csircentral.net/3133/1/Magnetoelectric%20coupling-induced.pdf
Gupta, Rekha and Shah, Jyoti and Chaudhary, Sujeet and Singh, Sukhbeer and Kotnala, Ravinder K. (2013) Magnetoelectric coupling-induced anisotropy in multiferroic nanocomposite (1-x)BiFeO3-xBaTiO(3). Journal of Nanoparticle Research , 15 (10). UNSP 2004-9. ISSN 1388-0764 |
|
| Relation |
http://npl.csircentral.net/3133/
|
|