Microstructural investigations on simulated intercritical heat-affected zone of boron modified P91-steel
IR@NML: CSIR-National Metallurgical Laboratory, Jamshedpur
View Archive InfoField | Value | |
Title |
Microstructural investigations on simulated intercritical heat-affected zone of boron modified P91-steel
|
|
Creator |
Khajuria, A
Akhtar, M Bedi, R Kumar, Rajneesh Ghosh, M Das, C R Albert, S K |
|
Subject |
Materials Science
|
|
Description |
Conventional P91 and boron modified P91-steels were considered in the present investigation. Using Gleeble, weld intercritical heat-affected zone (ICHAZ) was processed. Conventional microscopy was done along with electron back-scattered diffraction for both specimens. Lath boundary of martensite was more, and preferably oriented for P91B-ICHAZ than P91-ICHAZ. Lattice strain was high and lath mobility was low for P91B-ICHAZ in comparison to P91-ICHAZ. Large fraction of ferritic grain structure (39.1%) and small fraction of fresh martensitic grain structure (9.5%) in P91-ICHAZ, whereas small fraction of ferritic grain structure (10.7%) and large fraction of fresh martensitic grain structure (32.7%) in P91B-ICHAZ was observed. However, tempered martensite exhibited meager variation. These differences between ICHAZ simulations were attributed to the presence of 100ppm-boron in P91B-steel.
|
|
Publisher |
Maney Publishing
|
|
Date |
2020-06
|
|
Type |
Article
PeerReviewed |
|
Relation |
https://www.tandfonline.com/doi/full/10.1080/02670836.2020.1784543
http://eprints.nmlindia.org/8210/ |
|
Identifier |
Khajuria, A and Akhtar, M and Bedi, R and Kumar, Rajneesh and Ghosh, M and Das, C R and Albert, S K (2020) Microstructural investigations on simulated intercritical heat-affected zone of boron modified P91-steel. Materials Science and Technology, Online (IF-1.835).
|
|