Hardening of Steel Through High-Voltage Low-Current Energy Input
IR@CIMFR: CSIR-Central Institute of Mining and Fuel Research, Dhanbad
View Archive InfoField | Value | |
Title |
Hardening of Steel Through High-Voltage Low-Current Energy Input
|
|
Creator |
Mallick, Mousumi
Mitra, Swapan Kumar Basak, Debasish Roy, Nirmal Kumar Maity, Maity |
|
Subject |
Material Testing
|
|
Description |
A novel approach of high-voltage low-current energy input is applied for hardening of plain carbon eutectoid steel. Initial fine lamellar pearlitic structure disintegrates into four characteristic regions: lamellar pearlite often containing nucleated cementite spheroids (Region-I), fragmented cementite lamella in α-ferrite matrix (Region-II), submicroscopic cementite particles/clusters dispersed in α-ferrite matrix (Region-III), and supersaturated α-ferrite (Region-IV). At a particular applied voltage, structural refinement and matrix supersaturation (evolving martensite) progress concomitantly up to 5 min, followed by a reverse trend of coarsening and degeneration of martensite. The refinement effect and martensite-peak-broadening effect are augmented with increasing voltage up to 75 kV at which the highest hardness (429 HV) of the steel is achieved with treatment duration of 5 min. While primary hardening effect arises from the martensite region of stratified plate morphology (Region-IV), a secondary effect of hardening is resulted from the region containing dispersed submicroscopic cementite particles/clusters in α-ferrite matrix (Region-III). In addition, in the specimen exhibiting maximum hardening effect (at 75 kV, 5 min), as a unique feature, nanosized cementite particles also appear in Region-IV being dispersed in martensite matrix so as to provide further effect of dispersion hardening along with martensitic hardening.
|
|
Publisher |
John Wiley
|
|
Date |
2021-02
|
|
Type |
Article
PeerReviewed |
|
Identifier |
Mallick, Mousumi and Mitra, Swapan Kumar and Basak, Debasish and Roy, Nirmal Kumar and Maity, Maity (2021) Hardening of Steel Through High-Voltage Low-Current Energy Input. Steel Research International.
|
|
Relation |
http://cimfr.csircentral.net/2450/
|
|