| Creator |
Tripathi, BP
Kumar, M Shahi, VK |
|
| Subject |
Engineering; Polymer Science
|
|
| Description |
Recently, alkaline or anion-exchange membranes (AEMs) have attracted remarkable interest for direct methanol fuel cells (DMFCs) application, operated at intermediate temperature (100-200 degrees C). In this manuscript, we report synthesis of organic-inorganic hybrid anion-exchange silica precursor (AESP) with ammonium functionality by ring opening of glycidoxypropyltrimethylammonium chloride under mild heating condition. A simple and ecofriendly procedure based on sol-gel method was used for the preparation of hydroxide conductive organic-inorganic AESP-poly(vinyl alcohol) (PVA) cross-linked AEM in aqueous media. Developed AEMs were extensively characterized for their physicochemical and electro-chemical properties under DMFC operating conditions. These membranes were designed to possess all the required properties of highly ion conductive membrane, namely reasonable swelling, dimensional and oxidative strength, flexibility, low methanol permeability along with reasonable hydroxyl ion conductivity (7.57 x 10(-2) S cm(-1)) due to quaternary ammonium group functionality. Reported AEM-100 showed 7.57 x 10(-2) S cm(-1) membrane conductivity much higher than reported values (0.30-3.40 x 10(-2) S cm(-1)) for other AEMs in the literature. Moreover, from the selectivity parameter among all developed membranes, AEM-100 (100 wt% to PVA of AESP in the membrane matrix), exhibited best result for alkaline DMFC applications. (C) 2010 Elsevier B.V. All rights reserved.
|
|
| Publisher |
ELSEVIER SCIENCE BVAMSTERDAMPO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS
|
|
| Date |
2011-09-20T12:03:11Z
2011-09-20T12:03:11Z 2010 |
|
| Type |
Article
|
|
| Identifier |
JOURNAL OF MEMBRANE SCIENCE
0376-7388 http://hdl.handle.net/123456789/12210 |
|
| Language |
English
|
|