Structure development and crystallization behaviour of PP/nanoparticulate composite
Metadata of CSIR Papers
View Archive Info| Field | Value | |
| Title |
Structure development and crystallization behaviour of PP/nanoparticulate composite
|
|
| Creator |
Saujanya, C
Radhakrishnan, S |
|
| Subject |
Polymer Science
|
|
| Description |
The structure development and crystallization behaviour of polypropylene (PP) containing nanoparticles of calcium phosphate prepared by a new route based on matrix mediated control of growth and morphology was investigated by X-ray diffraction (XRD), optical microscopy and DSC techniques. The results obtained were compared with that of PP containing conventionally prepared calcium phosphate (CaP0). Both nanoparticle filled PP as well as CaP0 filled PP crystallized in monoclinic cr crystalline phase. However, considerable changes were observed in the relative intensities of the XRD peaks, especially the peak II (040 reflection), in the case of PP filled with nanosize calcium phosphate. The isothermal crystallization curves showed dramatic increase of crystallization rate and decrease in till value for PP/nanoparticulate composites resulting in a rapid decrease in the ultimate spherulite size as compared to PP/CaP0 samples. The nucleating efficiency was found to be dependent on the particle size as inverse exponential power law. These results were further confirmed by DSC analysis. The optical transparency of the PP/nanoparticle composites was found to be much higher than that containing conventional CaP0 for the same concentrations and this could be associated with the reduction in the PP crystallite size. (C) 2001 Elsevier Science Ltd. All rights reserved.
|
|
| Publisher |
ELSEVIER SCI LTDOXFORDTHE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, OXON, ENGLAND
|
|
| Date |
2011-09-24T08:36:07Z
2011-09-24T08:36:07Z 2001 |
|
| Type |
Article
|
|
| Identifier |
POLYMER
0032-3861 http://hdl.handle.net/123456789/24056 |
|
| Language |
English
|
|