Corrosion Protection Mechanism of Polyaniline Blended Organic Coating on Steel
IR@CECRI: CSIR-Central Electrochemical Research Institute, Karaikudi
View Archive Info| Field | Value | |
| Title |
Corrosion Protection Mechanism of Polyaniline Blended
Organic Coating on Steel
|
|
| Creator |
Sathiyanarayanan, S.
Jeyaram, R. Muthukrishnan, S. Venkatachari, G. |
|
| Subject |
Corrosion Science and Engineering
|
|
| Description |
Epoxy–coal tar coatings are widely used to protect steel structures exposed to marine atmosphere due to their good barrier
property. However, the presence of micropores and microcracks formed during the coating formation leads to failure of the coating
due to permeation of corrosive ions. In recent years, it has been established that the coatings containing polyaniline �PANI� is able
to protect pinholes and defects due to its passivating ability. Hence, a study has been made on the effect of polyaniline content �1
and 3%� in epoxy–coal tar coating on the corrosion protection of steel in 3% NaCl solution by electrochemical impedance
spectroscopy �EIS� studies. Both phosphate- and chloride-doped polyanilines were prepared by a chemical oxidative polymerization
method. From EIS studies, it has been found that the resistance value of the coatings containing 1 and 3% phosphate-doped
polyaniline and 3% chloride-doped polyaniline pigmented coatings are �109 � cm2 even after 90 days exposure to NaCl solution,
which are two orders high in comparison to that of conventional coal tar epoxy coatings. Besides, the conducting state of
polyaniline has been found to be decreased after exposure to NaCl solution due to redox property of PANI. X-ray photoelectron
spectroscopy studies have shown that polyaniline forms a complex layer with iron beneath the coating along with iron oxide.
|
|
| Publisher |
The Electrochemical Society
|
|
| Date |
2009
|
|
| Type |
Article
PeerReviewed |
|
| Format |
application/pdf
|
|
| Identifier |
http://cecri.csircentral.net/438/1/095-2009.pdf
Sathiyanarayanan, S. and Jeyaram, R. and Muthukrishnan, S. and Venkatachari, G. (2009) Corrosion Protection Mechanism of Polyaniline Blended Organic Coating on Steel. Journal of Electrochemical Society, 156 (4). pp. 127-134. |
|
| Relation |
http://cecri.csircentral.net/438/
|
|