Synthesis and characterization of Ca1-xSrxZr4(PO4)6 (0 less equal x less than 1) tape of NZP based low expansion ceramics
|
|
Creator |
Chakraborty, N
Chakrabarti, J Dasgupta, A Basu, Debabrata |
|
Subject |
Microstructure and Characterization
|
|
Description |
Different low thermal expansion ceramics of Ca1-xSrxZr4(PO4)6 system with x = 0, 0.25, 0.5 and 0.75 were synthesized by the solid state reaction method. After several heat treatments finished products were obtained at 1300¢XC. These were characterized for phase purity by X-ray Diffractometry and IR Spectroscopy. Densification parameters of the compositions with 3 and 5 wt% ZnO added as sintering aids were studied at 1100¢X, 1200¢X and 1300¢XC under soaking periods of 2-6 h. The corresponding effects on the physical, thermal and mechanical properties were observed. A maximum of 98% of theoretical density was obtained and flexural strength as high as 70 MPa was achieved. Thermal expansion varied from ¡V0.47 to 2.65 ¡Ñ 10¡V6/¢XC with increase in Sr content. The results are discussed in the light of the microstructures.
|
|
Publisher |
The Indian Ceramic Society
|
|
Date |
2004-01
|
|
Type |
Article
PeerReviewed |
|
Format |
application/pdf
|
|
Identifier |
http://cgcri.csircentral.net/549/1/chakraborty.pdf
Chakraborty, N and Chakrabarti, J and Dasgupta, A and Basu, Debabrata (2004) Synthesis and characterization of Ca1-xSrxZr4(PO4)6 (0 less equal x less than 1) tape of NZP based low expansion ceramics. Transactions of the Indian Ceramic Society, 63 (1). pp. 33-38. ISSN 0371-750X |
|
Relation |
http://cgcri.csircentral.net/549/
|
|