Structure, dielectric and optical properties of transparent Nd(3+):KNbO(3) nanocrystalline glass-ceramics
IR@CGCRI: CSIR-Central Glass and Ceramic Research Institute, Kolkata
View Archive InfoField | Value | |
Title |
Structure, dielectric and optical properties of transparent Nd(3+):KNbO(3) nanocrystalline glass-ceramics
|
|
Creator |
Saikia Chaliha, Reenamoni
Annapurna, K Tarafder, Anal Tiwari, V S Gupta, P K Karmakar, Basudeb |
|
Subject |
Glass
|
|
Description |
Here, glass in the composition of 25K2O–25Nb2O5–50SiO2 (mol%) doped with Nd2O3 (0.5 wt.% in excess)was isothermally crystallized at 800 C for 1–100 h. Their structures, dielectric and optical properties were analyzed with the progress of nanocrystallization of Nd3+: KNbO3 by XRD, FESEM, TEM, FTIRRS, DC, optical absorption and fluorescence measurements. Crystallization of KNbO3 is confirmed from XRD and the appearance of 749 cm-1 band in the FTIRRS spectra. The crystallite size estimated from
XRD and TEM is found to vary in the range 7–11 nm. The formation of ferroelectric nano-crystalline KNbO3 phase is also attributed by a steep rise in the dielectric constant (e) of glass–ceramics with heat-treatment time. The measured photoluminescence spectra have exhibited emission transitions of 4F3/2?4IJ (J = 9/2, 11/2 and 13/2) from Nd3+ ions upon excitation at 817 nm. It is observed that the photoluminescent intensity and excited state lifetime of Nd3+ ions initially decrease and then gradually increase with increase in heat-treatment time. The absorption spectra and fluorescence measurements disclose that the Nd3+ ions gradually enter into the KNbO3 nanocrystals.
|
|
Publisher |
Elsevier
|
|
Date |
2010-07
|
|
Type |
Article
PeerReviewed |
|
Format |
application/pdf
application/pdf |
|
Identifier |
http://cgcri.csircentral.net/631/1/annapurna'10.pdf
http://cgcri.csircentral.net/631/3/927%2DAT%2DOM.pdf Saikia Chaliha, Reenamoni and Annapurna, K and Tarafder, Anal and Tiwari, V S and Gupta, P K and Karmakar, Basudeb (2010) Structure, dielectric and optical properties of transparent Nd(3+):KNbO(3) nanocrystalline glass-ceramics. Optical Materials , 32 (9). pp. 1202-1209. ISSN 0925-3467 |
|
Relation |
http://cgcri.csircentral.net/631/
|
|