Synthesis, Characterization and Magnetic Properties of Nickel Ferrite by Soft Chemical Method
IR@CGCRI: CSIR-Central Glass and Ceramic Research Institute, Kolkata
View Archive Info| Field | Value | |
| Title |
Synthesis, Characterization and Magnetic Properties of Nickel Ferrite by Soft Chemical Method
|
|
| Creator |
Ghosh, Sushmita
Dasgupta, Subrata |
|
| Subject |
Microstructure and Characterization
|
|
| Description |
Synthesis of nanosized nickel ferrite by a template method where tartaric acid is used as a ligand and nitric acid as an oxidant is described. The synthesized powders were characterized by TGA, XRD, FTIR, TEM, BET, VSM and SQUID studies. The average crystallite size of the phase pure material was of 30 nm and the surface area was found to be 20.37 m(2).g(-1). Magnetic measurements of the phase pure powder were carried out at room temperature by VSM at a magnetic field of 1 Tesla, and by SQUID at a magnetic field of 6 Tesla. High saturation magnetization of 31.43 emu.g(-1) is observed in case of VSM and 43.36 emu.g(-1) is observed for SQUID measurements. Comparative analysis of M(s) values synthesized by different routes are compared.
|
|
| Publisher |
Indian Ceramic Society
|
|
| Date |
2010-03
|
|
| Type |
Article
PeerReviewed |
|
| Format |
application/pdf
|
|
| Identifier |
http://cgcri.csircentral.net/779/1/sushmita.pdf
Ghosh, Sushmita and Dasgupta, Subrata (2010) Synthesis, Characterization and Magnetic Properties of Nickel Ferrite by Soft Chemical Method. Transactions of the Indian Ceramic Society, 69 (1). pp. 25-28. ISSN 0371-750X |
|
| Relation |
http://cgcri.csircentral.net/779/
|
|