Ag-TiO(2) Nanoparticle Codoped SiO(2) Films on ZrO(2) Barrier-Coated Glass Substrates with Antibacterial Activity in Ambient Condition
IR@CGCRI: CSIR-Central Glass and Ceramic Research Institute, Kolkata
View Archive InfoField | Value | |
Title |
Ag-TiO(2) Nanoparticle Codoped SiO(2) Films on ZrO(2) Barrier-Coated Glass Substrates with Antibacterial Activity in Ambient Condition
|
|
Creator |
Mukhopadhyay, Anindita
Basak, Sujit Das, Jugal Kishore Medda, Samar Kumar Chattopadhyay, Krishnananda De, Goutam |
|
Subject |
Glass
|
|
Description |
Anatase TiO(2) and Ag nanoparticles (NPs) codoped SiO(2) films were prepared by the sol-gel method. Proportionate amounts of 3-(glycidoxypropyl)trimethoxysilane (GLYMO), tetraethylorthosilicate (TEOS) and 3-(methacryloxypropyl)trimethoxysilane (MEMO) derived inorganic organic silica sol, commercially available dispersed anatase TiO(2) NPs, and AgNO(3) were used to prepare the sols. The films were prepared on ZrO(2) (cubic) precoated soda-lime glass substrates by a single-dipping technique and heat-treated at 450 degrees C in air and H(2)/Ar atmosphere to obtain hard, relatively porous, and transparent coatings of thickness >600 nm. The ZrO(2) barrier layer was previously applied on soda-lime glass to restrict the diffusion of Ag into the substrate. The Ag-TiO(2) NPs incorporated SiO(2) films were intense yellow in color and found to be fairly stable at ambient condition for several days under fluorescent light. These films show a considerable growth inhibition on contact with the gram negative bacteria E. coli.
|
|
Publisher |
American Chemical Society
|
|
Date |
2010-09
|
|
Type |
Article
PeerReviewed |
|
Format |
application/pdf
|
|
Identifier |
http://cgcri.csircentral.net/816/1/anindita'10.pdf
Mukhopadhyay, Anindita and Basak, Sujit and Das, Jugal Kishore and Medda, Samar Kumar and Chattopadhyay, Krishnananda and De, Goutam (2010) Ag-TiO(2) Nanoparticle Codoped SiO(2) Films on ZrO(2) Barrier-Coated Glass Substrates with Antibacterial Activity in Ambient Condition. ACS Applied Materials & Interfaces, 2 (9). pp. 2540-2546. ISSN 1944-8244 |
|
Relation |
http://cgcri.csircentral.net/816/
|
|