Fabrication of simple and ring-type Piezo Actuators and their characterization
IR@NAL: CSIR-National Aerospace Laboratories, Bangalore
View Archive InfoField | Value | |
Title |
Fabrication of simple and ring-type Piezo Actuators and their characterization
|
|
Creator |
Sahoo, B
Panda, PK |
|
Subject |
Chemistry and Materials (General)
Electronics and Electrical Engineering |
|
Description |
A piezo multilayered stack of height 10mm is fabricated using 80 μm thick PZT tapes prepared by tape-casting technique. About 120 layers of thin tapes are dried, screen-printed with Pt-electrode paste, stacked, laminated, and then isopressed to obtain a green multilayered stack. Cofiring of the stack is carried out at 1250◦C for 1 h with very slow heating rate (15◦ per 1 h). The sintered stack
is poled at 2 kV per mm in hot (120◦C) silicone oil bath for 45 minutes, and free displacement and block force were characterized. The actuator generates free displacement of 10 μm (0.1% strain) and block force of 1427N at 175V. In a similar way, a ring-shaped multilayered PZT stack was fabricated; the displacement was measured to be 8 μm. The ring-type actuator is mainly used for fluid flow control in space vehicles.
|
|
Publisher |
Hindawi Publishing Corporation
|
|
Date |
2012
|
|
Type |
Journal Article
PeerReviewed |
|
Format |
application/pdf
|
|
Identifier |
http://nal-ir.nal.res.in/10452/1/Ring_Actuator%2Dpkpanda.pdf
Sahoo, B and Panda, PK (2012) Fabrication of simple and ring-type Piezo Actuators and their characterization. Smart Materials Research, 2012 . |
|
Relation |
http://dx.doi.org/10.1155/2012/821847
http://nal-ir.nal.res.in/10452/ |
|